Introduction to Tantalum Carbide TAC Powder
It is a light-brown metallic cubic crystal powder belonging to the sodium chloride cubic cristal system. The density is 14.3g/cm3.
It is insoluble when dissolved in water. It has a strong oxidation resistance, and is easily melted by potassiumpyrosulfate to decompose. Superconductivity is demonstrated by its high conductivity and resistance of 30O at normal room temperatures.
This is used for powder metalurgical, cutting tools and chemical vapor deposition. It also makes hard-wear-resistant alloy cutting tools. The tantalum carbide sintered body has a golden color, and can be used to decorate watches.
|Tantalum Carbide TaC Powder Properties|
|Other Names||tantalum(IV) carbide, TaC powder|
|Appearance||Powders from brown to dark brown|
|Boiling Point||4780-5470 degC|
|Solubility of H2O||Insoluble|
1. For TaC powder, mix tantalum pentoxide and solid carbon ball mills. At 1700, the mixture should be reduced and carburized in an oxygen-free atmosphere (mainly vacuum and argon atmospheres).
2. By heat treating in a non-oxidizing environment using the liquid precursor, nano tantalum caride powder was obtained. A small glass rod was used to stir 5mL of anhydrousethanol into a small vessel containing 0.50gTaCL5. The ultrasonic cleaner was heated to 55°C and operated at 40kHz. It produced 80W of power. After ultrasonic oscillation lasting 5-10min, 0.10g of nano-activated charcoal was added. The oscillation continued for 15-20min. Then, pour it into the crucible. Coat it well on the inner wall. Dry it with a hot fan. The crucible containing the sample was placed into a vacuum hot pressing furnace at 1300 in a 100Pa or hydrogen atmosphere. At 1400 in an argon atmosphere, the holding time is 0.55h and the heating speed is 20/min. Use a brush to brush the products in crucible after the experiment.
3. Tantalum pentoxide can be converted to heat in the atmosphere Potassium pyrosulfate can be fused. Tantalum and carbon, or tantalum pentoxide, and black in an inert environment heated to 1900 reaction.
4. Use tantalum pentoxide or methane as the reaction gases, argon to carry it, silicon carbide resistance against the external radiation heating or carbonization, tantalum pentoxide combined with carbon black, pressurized mold, heating in hydrogen, or vacuum.
Tantalum Carbide TaC Powder
It is widely used in industry as well as the military. It is used extensively in cemented carbide as an additive. Its primary function it to increase the high temperature strength of cemented carbide and to prevent the growth of tungsten-carbidide particles.
Use as a hard coating on cutting tools to increase the wear resistance and chemical resistance of the base material.
It can be used by the military as a coating on jet engine turbine blades.
It can be used as an electrode material due to its high conductivity. This is done by using electric discharge wires that are cut into intricate shapes.
The second phase of the particle reinforced metal matrix composites can be used in aerospace and metallurgy as well as for electric power, hydropower, mining, among other applications.
Main Supplier for Tantalum-Carbide TaC Powder
Technology Co. Ltd. is a trusted global supplier and manufacturer of chemicals and Nanomaterials. They have over 12 years experience in producing super high-quality chemicals, such as silicon powder.
Tantalum carbide TaC powder is available in high quality. Contact us today to make an inquiry. (firstname.lastname@example.org)